| ProductName |
： |
|
|
| Model |
： |
|
|
| Category |
： |
Series cycloaliphatic |
| Download |
： |
|
|
|
|
|
|
|
|
|
|
|
Name |
Color
（Garlock） |
Viscosity
（25℃） |
Density
（25℃） |
Amine value
mgKOH/g |
AHEW |
added weight in 100g standard resin |
Gel time
25℃/100g |
Thru drying time
（25℃） |
|
R-2251 |
3 |
40-60 |
0.95 |
315 |
87 |
46 |
115mins |
4.5hs |
|
R-2252 |
3 |
50-100 |
0.95 |
329 |
85 |
45 |
65mins |
4.0hs |
|
R-2253 |
2 |
300-400 |
0.98 |
320 |
92 |
49 |
38mins |
3.0hs |
|
R-2256 |
3 |
300-400 |
0.96 |
290 |
91 |
48 |
43mins |
3.5hs |
|
R-2257 |
2 |
350-450 |
1.03 |
312 |
98 |
52 |
18mins |
1.5hs |
|
R-2258 |
3 |
200-350 |
1.05 |
320 |
92 |
48 |
40mins |
3.5hs |
|
R-2259 |
2 |
400-500 |
1.05 |
310 |
97 |
51 |
27mins |
2.0hs |
|
R-2261 |
1 |
200-350 |
1.03 |
300 |
102 |
54 |
46mins |
3.8hs |
|
R-2265 |
1 |
350-500 |
1.03 |
300 |
97 |
51 |
62mins |
4.0hs |
|
R-2268 |
1 |
100-200 |
1.03 |
310 |
102 |
53 |
30mins |
3.0hs |
|
R-2269 |
1 |
250-350 |
1.03 |
302 |
102 |
54 |
48mins |
3.8hs |
|
R-2281 |
6 |
200-300 |
1.02 |
650 |
46 |
25 |
30mins |
2.5hs |
|
R-2282 |
1 |
5-10 |
1.02 |
610 |
43 |
23 |
35mins |
3.0hs |
|
R-2283 |
1 |
5-10 |
1.02 |
495 |
62 |
33 |
35mins |
3.0hs |
|
Name |
solidifying environment |
properties |
application |
|
R-2251 |
room temperature |
Durable, low viscosity, fast color, water-white-resistant,fine flexibility,bright in color. |
Flooring coating, solvent-free anti-corrosion coatings, casting materials, adhesives |
|
R-2252 |
room temperature |
Durable, fast-curing in later period, bright luster of condensate |
Flooring coating, electronic encapsulation |
|
R-2253 |
room temperature |
excellent water-resistant and weather-proof properties of condensate, fast curing, good wear resistance |
Flooring coating, anti-corrosion coating |
|
R-2256 |
room temperature |
no blanch under conditions of low temperature and moist condition, fast hardening, good flexibility |
Concrete repair, floor coating, casting materials |
|
R-2257 |
room temperature |
fast-curing at low temperature, weather-resistant, good smoothness and brightness of coating |
flooring and anti-corrosion coatings |
|
R-2258 |
room temperature |
high mechanical strength, fast hardening speed at low temperature, low-viscosity, good brightness, fine acid resistance |
flooring coatings, casting materials, battery end injecting glue |
| R-2259 |
room temperature |
High-gloss, no blanching, excellent chemical-resistant (especially acidic), fast-curing at low temperature |
flooring coating, battery end injecting glue |
|
R-2261 |
room temperature/warm up |
light-colored, fast color, good chemical resistance, high gloss |
flooring coatings, crystal glue, transparent electronic packaging materials |
| R-2265 |
room temperature |
excellent hardness, good weather resistance, fine smoothness and gloss, anti-moisture,high mechanical strength,good resistance to cooling and heating |
solar panel plastic packaging, flooring paint, outdoor flooring paint, color yarn coating |
| R-2268 |
room temperature |
low viscosity, fast curing, fine flexibility,no blanching of condensate |
artificial plants’water drop, color yarn flooring coating adhesive |
| R-2269 |
room temperature |
Low viscosity, fast-hardening, low odor(almost odorless), no volatile gas, low irritation, good weather resistance |
flooring coatings, crystal glue, transparent electronic materials, glass coatings |
|
R-2281 |
room temperature |
fine hardness, special H.D.T high, up to 150 ℃ against general E -51 solidifying temperature |
High-temperature-resistant electronic packaging materials, molding plastic, High-temperature-resistant coating |
|
R-2282 |
room temperature |
Light color, low viscosity, fine hardness and high Tg (130 ℃) and good weather-resistance |
High-temperature-resistant coatings, polished plastic, molding plastic |
|
R-2283 |
room temperature |
Light color, low viscosity, fine hardness, good weather-resistance, Tg temperature (93 ℃), can cure under room temperature |
temperature-resistant coatings, polished plastic |
| | |
|
|
| |